Synthesis and characterization of graphene oxide nanocomposite from coconut shell GO-Fe 3 O 4 has been done. Graphene oxide can be prepared using Hummer's method and Subsequently, the synthesis of GO-Fe 3 O 4 nanocomposite was carried out by ultrasound assisted co-precipitation of iron (II) and (III) chlorides in the presence of GO. The formation of GO and graphene-Fe 3 O 4 nanocomposite was confirmed by X-ray diffraction (XRD), Fourier transform-infrared (FTIR), SEM and Raman spectroscopy. The characteristics of GO-Fe 3 O 4 as a result of synthesis from coconut shell analyzed using XRD showed that GO characteristics peak in accordance with the characteristics of GO-Fe 3 O 4 in (JCPDS No. 88-0315). Analysis using FTIR was seen in 3421 cm -1 (O-H stretching), 1631 cm -1 (C = C aromatic), and 565 cm -1 (Fe-O). Analysis using SEM seen in the presence of Fe, O and C in the EDX analysis confirmed the formation of GO-Fe 3 O 4 nanocomposite. Analysis using Raman spectroscopy showed that peaks of Fe 3 O 4 were at wavelengths of 396 cm -1 because sp 3 carbon was bound to Fe 3 O 4 so that the peak band D was not present in GO-Fe 3 O 4 spectroscopy.
|Journal||IOP Conference Series: Earth and Environmental Science|
|Publication status||Published - 9 Jan 2019|
|Event||2nd International Conference on Collaboration Seminar of Chemistry and Industry, CoSCI 2018, in conjunction with 23rd Indonesian Society for Biochemistry and Molecular Biology, ISBMB 2018 - Surabaya, Indonesia|
Duration: 11 Oct 2018 → 12 Oct 2018