Characterization of vickers hardness and corrosion rate of stainless steel-316L coated with hydroxyapatite-polyvinyl alcohol

Aminatun, F. F.S.B. Tenong, D. Hikmawati, E. M. Setiawati

Research output: Contribution to journalConference articlepeer-review

2 Citations (Scopus)

Abstract

This study aims to determine the effect of variations in the composition of the hydroxyapatite-Poly Vinyl Alcohol (HA-PVA) coating to the Vickers hardness and the corrosion rate of SS316L. Cylindrical stainless steel-316L (SS316L), which has a diameter of 8mm and a thickness of 5mm, was sterilized by immersion in ethanol then rinsed using distilled water. The coating material is made from a mixture of HA-PVA with variations in the composition of A (27: 3), B (25: 5), C (20:10) and D (15:15) (in wt%) dissolved in 70% distilled water (in wt%). HA-PVA solution was coated on SS316L using airbrush spraying method at a pressure of 3.5x105 Pa, a nozzle diameter of 0.4 mm and a nozzle-sample distance of 10 cm. The test results show that the variations of the HA-PVA composition affect the hardness and the corrosion rate of SS316L. The more HA coating on the SS316L, the more it protects the SS316L substrate from corrosion. The conclusion show that the sample A with the HA-PVA composition of 27: 3 (in wt%) is found to be the best composition with a Vickers hardness of 2.43 VHN and a corrosion rate of 0.004 mm/year.

Original languageEnglish
Article number012012
JournalJournal of Physics: Conference Series
Volume1816
Issue number1
DOIs
Publication statusPublished - 8 Mar 2021
Event10th International Conference on Theoretical and Applied Physics, ICTAP 2020 - Mataram, West Nusa Tenggara, Indonesia
Duration: 20 Nov 202022 Nov 2020

Fingerprint

Dive into the research topics of 'Characterization of vickers hardness and corrosion rate of stainless steel-316L coated with hydroxyapatite-polyvinyl alcohol'. Together they form a unique fingerprint.

Cite this